High Quality Industrial Fiberglass Film Coated Filter Cloth (needled Felt)

Fiberglass filtration materials are made by fast pulling from the melted glass liquid. It is a kind of inorganic non-woven filtration material fiberglass is usually divided into two types: 1, aluminum boron silicate glass fiber, called non-alkali fiberglass(R2O-alkali metal oxide content in less...

Send InquiryChat Now
Product Details

image001.png


Fiberglass filtration materials are made by fast pulling from the melted glass liquid. It is a kind of inorganic non-woven filtration material fiberglass is usually divided into two types: 1, aluminum boron silicate glass fiber, called non-alkali fiberglass(R2O-alkali metal oxide content in less than 0.5%). 2, sodium-calcium silicate fiber called middle-alkali fiberglass(content of R2O-alkali metal oxide between 0.5%~1.2%). Compared with organic synthetic fibers, it has high tensile strength, and the elongation is relatively small. Fiberglass has very good temperature resistance. Its shrinkage at 280℃ is zero. Glass fiber can resist most of the chemicals except hydrofluoric acid, strong acid, and strong alkali at room temperature and the alkali at high temperature. But its resistance capability of hydrolysis is relative bad. Storing in the condition of 100% relative humidity for 128 days, the strength will reduce 16% and 21% for non-alkali and middle-alkali fiberglass.

Due to the special component of fiberglass, it does not have very good water and corrosion resistance. Its resistance to curving is also not good. Therefore the filtration materials contains fiberglass must apply the post-processing. That is to improve the combination between the felt layer and the fabric layer, protect the felt and fabric from corrosion. It will also improve the ability of dust stripping from the felt.

Based on different industry conditions, we can produce the filtration felt using fiberglass as fabric and combine different high-temperature fiber with fiberglass in certain proportion as the felt layer. The products are applied in blast furnace gas, calcium carbide, out let of cement kiln, cement grinding machine, preheated dryer and carbon filtration. We can provide product made by different formulation based on request of customers’ industry condition.


Polyester film coated needled felt

Material

Polyester fiber
     Polyester industrial filament base fabric
     PTFE Microporous membrane

Weight(g/m2)

550(g/㎡)

Thickness(mm)

1.8mm

Filtration wind speed

≤1m/min

Air Permeability(m3/m2/min)

2-6m3/㎡.min

Bulk Density(g/m2)

0.240g/㎡

Filtration precision

Dust particle size≥5µm
     Filtration efficiency100%

Tensile Strength(N/5×20cm)

Warp

>1000N/5×20㎝

Weft

>1800N/5×20㎝

Tensile Elongation(%)

Warp

<35%

Weft

<45%

Continuous Working Temperature

130℃

Instantaneous Working Temperature

150℃

Acid and alkali resistance

Good

Dust Stripping Rate(%)

96.67%

Static Dust Catching Rate(%)

99.965%

Dynamic Dust Catching Rate(%)

99.999%

Dynamic Resistance(%)

128Pa


Related Products
Inquiry

  • D7, Huashan Industrial Park, Xinfu District, Fushun City, Liaoning Province, China

  • PhoenixYY@aliyun.com

  • +86-024-58217958

Fushun New Oriental Industrial Filtration Material Co.,Ltd